TEMPERED GLASS



      When thinking of some of the world’s most dramatic, visually breathtaking buildings, they most likely involve large expanses of glass. Before these architectural masterpieces can be created, the glass may need to be heat-treated for durability and/or safety reasons. The type of processing required – heat strengthening or tempering – depends on the glass’ specific application. 

    There are two different types of heat treated glasses – heat-strengthened and tempered. The similarities between the two include: 

    Production using the same processing equipment. Heating the glass to approximately 1,200 degrees F, then force-cooling it to create surface and edge compression. 

    The differences between the two glasses are as follows: 

    · With tempered glass, the cooling process is accelerated to create higher surface compression [the dimension of force or energy per unit area] and/or edge compression in the glass. It is the air-quench temperature, volume, and other variables that create a surface compression of at least 10,000 pounds per square inch (psi). This is the process that makes the glass four to five times stronger and safer than annealed or untreated glass. As a result, tempered glass is less likely to experience a thermal break.

    · With heat-strengthened glass, the cooling process is slower, which means the compression strength is lower. In the end, heat-strengthened glass is approximately twice as strong as annealed, or untreated, glass.

    With tempered glass, the cooling process is accelerated to create higher surface compression [the dimension of force or energy per unit area] and/or edge compression in the glass. It is the air-quench temperature, volume, and other variables that create a surface compression of at least 10,000 pounds per square inch (psi). This is the process that makes the glass four to five times stronger and safer than annealed or untreated glass. As a result, tempered glass is less likely to experience a thermal break. With heat-strengthened glass, the cooling process is slower, which means the compression strength is lower. In the end, heat-strengthened glass is approximately twice as strong as annealed, or untreated, glass. 

    The industry standard specification requirements for heat treated or tempered glasses are ASTM C1048. For heat-strengthened glass – the requirement is a surface compression of 3,500 to 7,500 psi with no requirement for edge compression. Fully tempered glass will have either a minimum surface compression of 69 MPa (10,000 psi) or an edge compression of not less than 67 MPa (9,700 psi). 

    Safety glazings are typically specified to provide security or to keep occupants safe wherever there is the potential for broken glass to hurt people if it becomes a projectile, such as in a fire, explosion, tornado or hurricane.

    Heat-strengthened glass is typically specified when additional strength is needed to resist wind pressure, thermal stress or both and the additional strength or safety break pattern of fully tempered glass is not required. Another advantage of heat-strengthened glass is that when broken, the glass fragments are more similar in size and shape to annealed glass fragments and thus tend to stay in the opening longer than fully tempered glass particles. Although heat-strengthened glass is NOT a safety glazing by building code, this breakage pattern prevents the glass from falling and injuring someone.

    Safety glazing is fully tempered glass that meets the requirements of the safety glazing standard CPSC 16 CFR 1201 or ANSI Z97.1, or both. Safety glazing, when broken, fractures into relatively small pieces, thereby greatly reducing the likelihood of serious cutting or piercing injuries in comparison to ordinary annealed glass. For some applications, such as glass in doors, tub and shower enclosures and fixed glass in close proximity to a walking surface, fully tempered safety glass is required by building codes and ordinances. Fully tempered safety glass is often used for other applications where its strength and/or safety characteristic are desirable, such as table tops, counter tops, showcase enclosures, refrigeration and food service equipment, furniture and similar applications. Fully tempered glass also is used in applications when significant additional strength is needed to resist wind pressure, thermal stress or both.



    However, because of this break pattern, tempered glass is much more likely to fall from the glazing system immediately upon breakage. It’s essential for design professionals to consider this when selecting a safety glass. If it’s important for the glass to stay anchored in the glazing system, another form of safety glass, such as laminated glass, should be considered.

    With both heat strengthening and tempering, distortion is a possibility. Optical image distortion occurs in glass for many reasons, including glazing pressure, wind load, temperature and barometric pressure changes – or even changes in altitude between where a glass is made and where it is installed. Because of its fluidity at higher temperatures, glass also is inherently susceptible to roller wave, bow and warp while it is being heat-treated.

    That’s why doing full-scale mock-ups under job-site conditions is recommended to evaluate the optical aesthetics of a specific heat-treating process. In addition, the following tips are suggested in order to minimize the potential impact of glass distortion that is inherent with heat-treating processes:

    · Produce all heat-treated glass for a given project on the same equipment, using the same processing parameters

    · Glass distortion may also occur due to strain patterns in heat-treated glass or interference fringe patterns in the fabrication of insulating glass units.

    · Use thicker glass, as it is less prone to distortion · Orient heat-treated glass so that roller wave [the periodic wave imparted to glass during heat-treatment, measured by the peak-to-valley distance] is parallel to the window sill/header.

    While there is no industry standard to quantify permissible heat-treated glass roller wave, a tolerance of 0.005 inches is often specified. PPG recommends using a millidiopter specification, if it is available, instead.


    Safety is a prime consideration when determining the type of heat treating process necessary for a project. Deciding whether to use heat strengthened or tempered glass depends on the specific application. For example, heat-strengthened glass can be selected for applications that do not specifically require a safety glass product; and tempered glass should be used wherever safety glass is a requirement.


       Parameter:

    ■ T=Transmittance

    ■ R=Reflectivity

    ■ SHGC=Solar Heat Gain Coefficient

    ■ SC=Shading Coefficient


    The glass performance data based on USA standard:NFRC 100-2010,European standard:CEN 



    Glass Configuration

    Visible Light

    Solar Energy

    U-Values

    U-Values

    SC

    SHGC

    STC

    LT

    LR

    DET

    ER

    EA

    Winter

    Summer

    EN673

    (%)

     Outside

    (%)

     inside

    (%)

    (%)

    (%)

    (%)

    (W/m2 K)

    (W/m2 K)

    (W/m2 K)

    G/G(3)

    (SF)

    (dB)

    3mm float Clear glass

    90

    8

    8

    85

    8

    7

    5.91 

    5.33 

    5.83 

    1.00 

    0.88 

    29

    4mm float Clear glass

    90

    8

    8

    84

    8

    8

    5.88 

    5.30 

    5.80 

    0.99 

    0.87 

    29

    5mm float Clear glass

    90

    8

    8

    83

    8

    9

    5.84 

    5.27 

    5.70 

    0.98 

    0.86 

    30

    6mm float Clear glass

    89

    8

    8

    80

    7

    13

    5.81 

    5.24 

    5.70 

    0.97 

    0.84 

    31

    8mm float Clear glass

    88

    8

    8

    77

    7

    16

    5.74 

    5.19 

    5.70 

    0.94 

    0.82 

    33

    10mm float Clear glass

    87

    8

    8

    74

    7

    19

    5.67 

    5.13 

    5.60 

    0.92 

    0.80 

    34

    12mm float Clear glass

    86

    8

    8

    72

    7

    21

    5.61 

    5.07 

    5.50 

    0.90 

    0.78 

    36

    15mm float Clear glass

    85

    8

    8

    69

    7

    24

    5.51 

    4.99 

    5.40 

    0.87 

    0.76 

    38

    3mm Clear+0.38PVB+3mm Clear

    89

    8

    8

    73

    8

    19

    5.75 

    5.19 

    5.67 

    0.91 

    0.79 

    35

    4mm Tempered Clear Glass+0.38PVB

    +4mm Tempered Clear Glass

    88

    8

    8

    70

    8

    22

    5.68 

    5.13 

    5.61 

    0.88 

    0.77 

    35

    5mm Tempered Clear Glass+0.76PVB

    +5mm Tempered Clear Glass

    86

    8

    8

    67

    7

    26

    5.56 

    5.03 

    5.49 

    0.86 

    0.75 

    36

    5mm Tempered Clear Glass+1.52PVB

    +5mm Tempered Clear Glass

    85

    8

    8

    66

    7

    27

    5.45 

    4.94 

    5.39 

    0.86 

    0.75 

    38

    5mm Tempered Clear Glass+1.9PVB

    +5mm Tempered Clear Glass

    84

    8

    8

    64

    7

    29

    5.39 

    4.89 

    5.34 

    0.84 

    0.73 

    39

    5mm Tempered Clear Glass+2.28PVB

    +5mm Tempered Clear Glass

    84

    8

    8

    63

    7

    30

    5.34 

    4.85 

    5.29 

    0.83 

    0.73 

    40

    6mm Tempered Clear Glass+0.76PV

    B+6mm Tempered Clear Glass

    85

    8

    8

    65

    7

    28

    5.50 

    4.98 

    5.43 

    0.85 

    0.74 

    38

    6mm Tempered Clear Glass+1.52PVB

    +6mm Tempered Clear Glass

    84

    8

    8

    64

    7

    29

    5.39 

    4.89 

    5.33 

    0.84 

    0.73 

    39

    6mm Tempered Clear Glass+1.9PVB

    +8mm Tempered Clear Glass

    83

    8

    8

    63

    7

    30

    5.33 

    4.84 

    5.28 

    0.83 

    0.73 

    40

    6mm Tempered Clear Glass+2.28PVB

    +9mm Tempered Clear Glass

    82

    8

    8

    62

    7

    31

    5.28 

    4.80 

    5.23 

    0.83 

    0.72 

    41

    Glass Configuration

    Visible Light

    Solar Energy

    U-Values

    U-Values

    SC

    SHGC

    STC

    LT

    LR

    DET

    ER

    EA

    Winter

    Summer

    EN673

    (%)

     Outside

    (%)

     inside

    (%)

    (%)

    (%)

    (%)

    (W/m2 K)

    (W/m2 K)

    (W/m2 K)

    G/G(3)

    (SF)

    (dB)

    4mm Tempered Clear Glass+9A

    +4mm Tempered Clear Glass

    82

    15

    15

    69

    14

    17

    2.87 

    3.00 

    3.00 

    0.87 

    0.76 

    33

    4mm Tempered Clear Glass+12A

    +4mm Tempered Clear Glass

    82

    15

    15

    69

    14

    17

    2.73 

    2.87 

    2.84 

    0.87 

    0.76 

    33

    5mm Tempered Clear Glass+12A

    +5mm Tempered Clear Glass

    80

    14

    14

    66

    12

    22

    2.71 

    2.86 

    2.83 

    0.85 

    0.74 

    34

    5mm Tempered Clear Glass+12Ar(Argon)

    +5mm Tempered Clear Glass

    80

    14

    14

    66

    12

    22

    2.55 

    2.72 

    2.66 

    0.85 

    0.74 

    34

    5mm Tempered Clear Glass+12A

    +5mm Low-E(EA)glass 

    75

    18

    17

    56

    14

    30

    1.90 

    1.92 

    1.90 

    0.80 

    0.70 

    34

    5mm Tempered Clear Glass

    +12Ar(Argon)+5mm Low-E(EA)glass

    75

    18

    17

    56

    14

    30

    1.62 

    1.63 

    1.59 

    0.81 

    0.70 

    34

    5mm Ocean blue glass +12Ar(Argon)

    +5mm tempered clear glass 

    54

    10

    14

    41

    8

    51

    2.55 

    2.72 

    2.66 

    0.59 

    0.52 

    34

    5mm  Ocean blue glass+12Ar(Argon)

    +5mm Low-E(EA) glass 

    50

    11

    16

    34

    9

    57

    1.62 

    1.63 

    1.59 

    0.54 

    0.47 

    34

    5mm blue star gray tinted

    +12Ar(Argon)+5mm Clear

    43

    9

    13

    38

    8

    54

    2.55 

    2.72 

    2.66 

    0.57 

    0.49 

    34

    5mm blue star gray tinted+12Ar(Argon)

    +5mm Low-E(EA)glass 

    40

    10

    16

    32

    9

    59

    1.62 

    1.63 

    1.59 

    0.51 

    0.45 

    34

    5mm  Ocean blue reflective+12A

    +5mm  Clear glass

    19

    23

    49

    21

    16

    63

    2.36 

    2.47 

    2.44 

    0.37 

    0.32 

    34

    5mm Ocean blue reflective 

    +12Ar(Argon)+5mm  Clear glass

    19

    23

    49

    21

    16

    63

    2.15 

    2.28 

    2.22 

    0.36 

    0.31 

    34

    6mm Clear+9A+6mm Clear glass 

    80

    14

    14

    64

    12

    24

    2.84

    2.97

    2.97 

    0.84 

    0.73 

    34

    6mm Clear+12A+6mm Clear glass 

    80

    14

    14

    64

    12

    24

    2.70 

    2.84 

    2.81 

    0.84 

    0.73 

    35

    6mm Ocean blue glass+12Ar (Argon)

    +6mm  Clear glass

    49

    8

    13

    36

    7

    57

    2.53 

    2.70 

    2.65 

    0.55 

    0.48 

    35

    6mm Ocean blue glass+12Ar (Argon)

    +6mm Low-E(EA) glass 

    50

    11

    15

    33

    9

    58

    1.62 

    1.63 

    1.59 

    0.54 

    0.47 

    35

    6mm blue star gray tinted+12Ar(Argon)

    +6mm Clear glass 

    40

    8

    13

    35

    8

    57

    2.53 

    2.70 

    2.65 

    0.53 

    0.46 

    35

    6mm blue star gray tinted+12Ar(Argon)

    +6mm Low-E(EA)glass 

    45

    9

    14

    30

    8

    62

    1.62 

    1.62 

    1.59 

    0.49 

    0.43 

    35

    6mm blue star gray Reflective+12A

    +6mm Clear glass 

    19

    14

    32

    22

    13

    65

    2.66 

    2.80 

    2.77 

    0.40 

    0.35 

    35

    6mm blue star gray Reflective

    +12Ar(Argon)+6mm Clear glass 

    19

    14

    32

    22

    13

    65

    2.48 

    2.65 

    2.59 

    0.39 

    0.34 

    35

    According to the standard, U value in winter with U (winter and summer) night at U (Xia Zhou) two parameters to measure, when not specifically indicate when the U value is U (winter).